新型光固化硅橡胶复合材料的配方研究
|
Abstract:
为了获得绝缘性能良好、施工简单的电缆包覆材料，研究了适于光固化快速成型的硅橡胶复合材料的配方，利用紫外光固化技术在铁片上形成不同配方的硅橡胶复合材料涂层。涂层采用电子扫描显微镜(SEM)表征了体系固化后的微观结构，用红外光谱(IR)对体系的成分进行研究，结果表明在配方为热固性树脂复合物：聚丙烯酸酯基硅氧烷 = 7:3或8:2、光引发剂用量为2%时，可以在铁片表面形成致密、均匀、稳定的涂层。
In this study, the silicone rubber composites suitable for photo-curing and rapid prototyping were developed for the sake of cable insulation. The coatings were formed on the iron plate by UV curing technology. The microstructure of the system was characterized by an electron scanning microscope, and the composition of the system was studied by infrared spectroscopy. The experimental results showed that in the formulation of thermosetting resin composite: Polyacrylate ester siloxane = 7:3 or 8:2, the dense, uniform and stable coatings could be formed on the iron surface, with the adding. amount of 2wt% photoinitiator.
| [1] | 王煦, 王红梅, 袁德华. 包覆材料对铝包钢线耐腐蚀性能的影响[J]. 电线电缆, 2023(5): 12-16. |
| [2] | 景巍巍, 谢坤, 李鸿泽, 等. 硅橡胶绝缘高压电缆附件的老化特性研究[J]. 高压电器, 2023, 59(11): 201-210, 223. |
| [3] | 王景兵, 张帆, 程兆璐, 等. 盐雾对电缆附件硅橡胶电气绝缘性能影响及其机理[J]. 中国电力, 2023, 56(6): 82-89, 100. |
| [4] | 凌颖, 黄嘉盛, 李濛, 等. 基于硅橡胶基调控的高压电缆缓冲层缺陷修复研究[J]. 广东电力, 2023, 36(7): 84-93. |
| [5] | 张巍, 韩圣斌, 李秀峰, 等. 热老化下涂覆硅脂对110kV电缆终端接头界面电-热-力场的影响[J]. 绝缘材料, 2024, 57(6): 76-85. |
| [6] | 刘宗喜, 欧阳本红, 陈铮铮, 等. 钛酸铜钙改性硅橡胶对500kV直流电缆接头优化设计关键控制参数的改善研究[J]. 高压电器, 2023, 59(10): 153-161. |
| [7] | 陈述慧, 梅启林, 丁国民, 等. 丙烯酸共聚改性液态丙烯酸酯树脂及其复合材料力学性能研究[J]. 复合材料科学与工程, 2024(5): 12-18. |
| [8] | 张万里, 郑刚, 孙斌, 等. 乙烯-三氟氯乙烯共聚物的制备及其在电线电缆上的应用进展[J]. 材料导报, 2019, 33(z2): 609-612. |
| [9] | 王珍, 韩玉玺, 王忠卫, 等. 含氮光引发剂对丙烯酸酯涂料光固化性能的影响[J]. 涂料工业, 2023, 53(11): 1-7, 15. |